Investigation of electromagnetic shielding effectiveness of needle punched nonwoven fabric produced from conductive silver coated staple polyamide fibre.

Ozen, Mustafa Sabri, Sancak, Erhan, Soin, Navneet ORCID: 0000-0002-0196-2071, Shah, Tahir H. and Siores, E. ORCID: 0000-0003-2971-9580 (2016) Investigation of electromagnetic shielding effectiveness of needle punched nonwoven fabric produced from conductive silver coated staple polyamide fibre. Journal of the Textile Institute, 107 (7). pp. 912-922. ISSN 0040-5000

Full text not available from this repository.
Official URL: http://dx.doi.org/10.1080/00405000.2015.1070604

Abstract

In this paper, electromagnetic shielding effectiveness (EMSE) of needle-punched nonwoven fabric produced from silver-coated staple polyamide fibre having a fineness of 1.7 dtex was investigated. This production was carried out at Automatex needle punching line, which consists of carding, cross lapper and needle punching machine. After production, the surface resistivity measurements of needle-punched nonwoven fabric was carried out in accordance with ASTM D 257-07 standard. The EMSE of the as-produced needle-punched nonwoven fabric was determined using a network analyzer as specified in ASTM D4935-10 in the frequency range of 15–3000 MHz. Electromagnetic shielding test shows that needle-punched nonwoven fabric produced from 1.7-dtex silver-coated polyamide fibre has the highest shielding value of 36.53 dB in the frequency range of 15–3000 MHz. The EMSE of needle-punched nonwoven fabric with fibre fineness of 1.7 dtex increased from 11.00 dB maximum to 36.53 dB in the 15–3000 MHz frequency range. It was seen that as the frequency increases, reflection values of the needle-punched nonwoven fabric decrease at floating mode, while absorption values of the nonwoven fabric increase at floating mode in the frequency range of 15–3000 MHz. EMSE results of the needle-punched nonwoven fabric produced from 1.7-dtex silver-coated staple polyamide fibres were compared to carbon fabric and needle-punched nonwoven fabric made from stainless steel fibres.

Item Type: Article
Uncontrolled Keywords: silver coated polyamide fibre, needle punching, electromagnetic shielding and nonwoven
Divisions: University of Bolton Research Centres > Institute for Materials Research and Innovation
Depositing User: Tracey Gill
Date Deposited: 16 May 2016 13:24
Last Modified: 01 Jun 2018 08:10
Identification Number: 10.1080/00405000.2015.1070604
URI: http://ubir.bolton.ac.uk/id/eprint/863

Actions (login required)

Edit Item Edit Item